| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-792 | 0.953 | g/cm3 | |
| 流动率 | 190℃/21.6kg | ASTM D-1238 | 33 | g/10min | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.38 | g/10min | |
| 机械性能 | 屈服伸长率 | ASTM D-638 | 7 | % | |
| 断裂伸长率 | ASTM D-638 | 1000 | % | ||
| 硬度 | ASTM D-2240 | 61 | Shore D | ||
| 拉伸冲击强度 | ASTM D-1822,Type S | 80(168) | ft·lb/in2(kJ/m2) | ||
| 断裂拉伸强度 | ASTM D-638 | 4500(31) | psi(MPa) | ||
| 耐环境应力开裂性 | 122oF(50℃),F50,100%lgepal | ASTM D-1693 | 80 | hrs | |
| 2%割线弯曲模量 | ASTM D-790 B | 145,000(1000) | psi(MPa) | ||
| 屈服拉伸强度 | ASTM D-638 | 3900(27) | psi(MPa) | ||
| 热性能 | DSC熔点 | Dow Method | 268(131) | oF(℃) | |
| 脆化温度 | ASTM D-746 | <-105(<-76) | oF(℃) | ||
| DSC结晶点 | Dow Method | 244(118) | oF(℃) | ||
| 热变形温度 | 66psi(0.45MPa) | ASTM D-648 | 163(73) | oF(℃) | |
| 维卡软化点 | ASTM D-1525 | 264(129) | oF(℃) | ||